| 牌号 | 00952 |
|---|---|
| 厂家 | 沙特埃克森美孚 |
| 用途级别 | 薄膜 |
| 品牌 | 埃克森美孚 |
| 型号 | HDPE |
| 规格级别：薄膜 |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | HLMI | ASTM D-1238 | 9 | g/10min | ||
| 密度 | ASTM D-1505 | 0.952 | g/cm3 | |||
| 熔体流动速率 | 0.05 | g/10min | ||||
| 机械性能 | 拉伸断裂伸长率 | MD | ASTM D-882 | 400 | % | |
| TD | ASTM D-882 | 500 | % | |||
| 门氏撕裂强度 | MD | 12 | g | |||
| TD | 60 | g | ||||
| 1%割线模量 | MD | ASTM D-882 | 1250 | MPa | ||
| TD | ASTM D-882 | 1500 | MPa | |||
| 拉伸断裂强度 | MD | ASTM D-882 | 60 | MPa | ||
| TD | ASTM D-882 | 56 | MPa | |||
| 拉伸屈服强度 | MD | ASTM D-1505 | 33 | MPa | ||
| TD | ASTM D-1505 | 31 | MPa | |||
| Dart冲击强度 | F50 | ASTM D-1709 | 180 | g | ||
| 热性能 | 维卡软化点 | ASTM D-1525 | 125 | ℃ | ||
备注:特性：垂伸性好和挤出性好、高强度、高劲度